8Cr4Mo4V高溫合金軸承鋼
發布者：
yhjs999 發布時間：2024-01-11 09:45:04 訪問次數：95
|
牌號
|
8Cr4Mo4V高溫合金軸承鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
B20440
|
|
|
|
|
|
|
|
|
|
|
|
|
|
其他名稱
|
HCr4Mo4V M50
|
|
|
|
|
|
|
|
|
|
|
|
|
|
舊牌號
|
Cr4Mo4V
|
|
|
|
|
|
|
|
|
|
|
|
|
|
對應標準
|
YB 4105-2000
|
|
|
|
|
|
|
|
|
|
|
|
|
|
航空發動機用高溫軸承鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
High temperature bearing steel for aircraft engine
|
|
|
|
|
|
|
|
|
|
|
|
|
|
歸類
|
軸承鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
標簽
|
高溫合金軸承鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
說明
|
本標準適用于航空發動機軸承用高溫軸承鋼的熱軋或鍛制圓鋼、冷拉圓鋼（直條或盤狀）和鋼絲。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
8Cr4Mo4V 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
Mo
|
W
|
V
|
Co
|
O
|
|
最小值
|
0.75
|
-
|
-
|
-
|
-
|
3.75
|
-
|
-
|
4
|
-
|
0.9
|
-
|
-
|
|
最大值
|
0.85
|
0.35
|
0.35
|
0.015
|
0.008
|
4.25
|
0.2
|
0.2
|
4.5
|
0.25
|
1.1
|
0.25
|
1.00E-05
|
|
其他名稱為曾用牌號
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
8Cr4Mo4V 機械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
熱處理或狀態
|
硬度
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HBW
|
|
|
|
|
|
|
|
|
|
|
|
|
|
退火
|
197~241
|
|
|
|
|
|
|
|
|
|
|
|
|
|
注：小于10mm的鋼材，硬度測定法由供需雙方協議。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|