湖南Sanicro 69山特維克ENiCrFe-7鎳基焊條
Sanicro 69 是一種堿性藥皮焊條，用于大多數低合金鋼和不銹鋼上耐腐蝕堆焊。它還用于合金 690 型的合金，例如
Sanicro 69 和異種接頭的焊接。
該焊條具有優良的焊接性能，非常適合接頭焊接以及堆焊。
STANDARDS
– ISO 14172: Ni 6152
– AWS A5.11/ASME SFA-5.11: ENiCrFe-7
APPLICATIONS
It is used for welding of alloys of Alloy 690 type (e.g. Sanicro 69) and dissimilar joints. It is also used for overlaywelding in the nuclear industry used primarily for steam generators in nuclear power plants (PWR). For thisapplication the material is characterized by extremely high stress corrosion resistance in primary side PWR waterconditions. Sanicro 69 also has improved pitting resistance in chloride containing solutions compared to alloy 600.
Sanicro 69 is characterized by excellent resistance to nitric acid. Furthermore, the material shows very goodresistance to high temperature oxidation.
焊縫金屬特征
以下數據對非熱處理的全焊縫金屬有效。
C Si Mn P S Cr Ni Mo Fe Nb
化學成分，wt%
≤0.040 0.5 2.4 ≤0.015 ≤0.005 30 56 ≤0.3 9 1.6
微觀組織 - 全焊縫金屬
全奧氏體
機械性能
溫度 C (°F) 20 (68) 360 (680)*
屈服強度，R MPa (ksi) 420 (61) 330 (48)
抗拉強度，R MPa (ksi) 650 (94) 520 (75)
延伸率，A % 43 39
沖擊強度，夏比 V 型 J (ft lb) 115 (85) -
R 對應于 0.2% 塑型變形的屈服強度
o b
P0.2a
m
a p0.2
免責聲明：建議僅供參考，針對特定應用場合的焊材適用性我們需要了解實際服役條件后才能予以確認。因持續研發導致的產品
技術數據更改不會另行通知。該數據表僅適用于山特維克焊材。
b 610°C 下焊后熱處理 16 h 后。
耐腐蝕性能
抗晶間應力腐蝕開裂性。
制造
直徑，mm (in.) 電流，A
2.50 (~3/32) 50-70
3.25 (~1/8) 70-100
4.00 (~5/32) 105-145
必要時重新烘干焊條：200°C (390°F)/2 h
PRODUCTIVITY DATA
Electrode diameter, mm (in.) 2.50 (~3/32) 3.2 (~1/8) 4.00 (~5/32)
Length, mm (in.) 300 (~12) 350 (~14) 350 (~14)
Deposition rate
kg weld metal/h (approx.) ≤0.9 ≤1.4 ≤2.2
lb weld metal/h (approx.) ≤2.0 ≤3.1 ≤4.9
Effective value
kg weld metal/kg electrodes 0.66 0.69 0.67
lb weld metal/lb electrodes 0.66 0.69 0.67
Change value
Electrodes/kg weld metal 94 49 30
Electrodes/ lb weld metal 43 23 14
Burn-off time per electrode at max current, s 46 59 76
|
不銹鋼 焊條 |
308L/MVR |
E308L-17 |
0.02 |
0.8 |
1.0 |
20.0 |
10.5 |
|
|
308L/MVR |
E308L-15 |
0.03 |
0.2 |
1.7 |
20.0 |
10.0 |
|
|
|
308L/MVR |
E308L-16 |
0.03 |
0.3 |
1.5 |
20.0 |
10.0 |
|
|
|
308/308H |
E308H-17 |
0.06 |
0.7 |
1.1 |
20.0 |
10.0 |
|
|
|
347/MVNb |
E347-17 |
0.02 |
0.8 |
0.8 |
19.5 |
10.0 |
|
|
|
347/MVNb |
E347-15 |
0.06 |
0.2 |
1.7 |
19.5 |
10.0 |
|
|
|
316L/SKR |
E316L-17 |
0.02 |
0.8 |
1.1 |
18.5 |
12.0 |
2.8 |
|
|
316L/SKR |
E316L-15 |
0.03 |
0.2 |
1.7 |
18.5 |
12.0 |
2.8 |
|
|
316L/SKR |
E316L-16 |
0.02 |
0.3 |
1.4 |
19.0 |
12.0 |
2.8 |
|
|
316/316H |
E316H-17 |
0.06 |
0.8 |
1.0 |
19.0 |
12.0 |
2.8 |
|
|
318/SKNb |
E318-17 |
0.02 |
0.8 |
0.8 |
18.5 |
12.0 |
2.8 |
|
|
318/SKNb |
E318-15 |
0.04 |
0.2 |
2.1 |
18.5 |
12.5 |
2.7 |
|
|
317L/SNR |
E317L-17 |
0.02 |
0.7 |
0.9 |
19.0 |
13.0 |
3.7 |
|
|
2205 |
E2209-17 |
0.02 |
0.8 |
0.7 |
23.0 |
9.5 |
3.0 |
|
|
2205 |
E2209-15 |
0.02 |
0.5 |
0.8 |
23.0 |
9.5 |
3.0 |
|
|
904L |
E385-17 |
0.02 |
0.8 |
1.2 |
20.5 |
25.0 |
4.5 |
|
|
383 |
E383-17 |
0.02 |
0.9 |
0.9 |
27.0 |
32.0 |
3.7 |
|
|
P12-R |
EniCrMo-12 |
0.02 |
0.4 |
0.4 |
21.5 |
|
9.5 |
|
|
P625 |
EniCrMo-3 |
0.02 |
0.5 |
0.2 |
21.5 |
|
9.5 |
|
|
307 |
E307-17 |
0.07 |
0.8 |
4.0 |
20.0 |
10.5 |
0.8 |
|
|
309L |
E309L-15 |
0.03 |
0.2 |
1.9 |
24.0 |
13.0 |
|
|
|
P5 |
E309MoL-17 |
0.02 |
0.8 |
1.1 |
22.5 |
13.5 |
2.7 |
|
|
P5 |
E309MoL-15 |
0.03 |
0.2 |
2.0 |
22.5 |
13.0 |
2.7 |
|
|
P5 |
E309MoL-16 |
0.03 |
0.3 |
1.4 |
22.5 |
13.5 |
2.7 |
|
|
P7 |
E312-17 |
0.09 |
0.8 |
0.8 |
29.0 |
9.5 |
|
|
|
P10 |
ENiCrFe-3 |
0.02 |
0.4 |
6.5 |
16.0 |
|
|
|
|
309 |
E309-17 |
0.05 |
0.8 |
1.0 |
24.0 |
13.5 |
|
|
|
310 |
E310-17 |
0.10 |
0.5 |
2.1 |
26.0 |
21.0 |
|
|
|
310 |
E310-15 |
0.12 |
0.3 |
2.4 |
25.5 |
21.0 |
|