英國進(jìn)口MWA鑄鐵焊條Mac Cast E407|ENiFe-CI|鑄鐵焊接|壓力容器焊接

High strength machinable electrode for joining and building up on cast irons. Low amperage, smooth arc, minimum spatter and high resistance to cracking. Due to Bi-metallic core wire this product gives excellent current carrying capacity which will prevent overheating. For the repair of grey, S.G., nodular or ductile irons where higher strength is required. Also suitable for joining cast iron to mild steel (in conjunction with Mac Groove 71), pressure vessels, etc. Also available as a MIG wire.

高強(qiáng)度可加工Ni55鎳鐵焊條，用于鑄鐵的連接和堆焊。電流低，電弧平滑，飛濺小，抗裂性高。由于雙金屬芯線，該產(chǎn)品具有出色的載流能力，可防止過熱。用于需要更高強(qiáng)度的灰口鑄鐵、球墨鑄鐵的修復(fù)。也適用于連接鑄鐵和低碳鋼（與Mac Groove E71切割焊條一起使用）、壓力容器等。有對應(yīng)MIG焊絲可供選擇。

典型應(yīng)用：發(fā)動機(jī)缸體、氣缸蓋、泵殼、電機(jī)外殼、齒輪箱、機(jī)器底座、法蘭、凸輪、桿類、填充孔、鑄造輪齒修復(fù)以及堆焊或更換缺失部分。

Typical All Weld Metal Chemical Analysis (%)

典型全焊縫金屬成分

Typical All Weld Metal Mechanical Properties（As Welded）

典型全焊縫金屬機(jī)械性能（焊態(tài)）：

Tensile Strength抗拉強(qiáng)度： 448 N/mm²

Elongation延伸率： 20%

Hardness硬度： 180 HB

Sizes Available and Recommended Amperages

尺寸Φ/電流：

Current電流：AC/DC (+)

Related Specification參考標(biāo)準(zhǔn)：AWS A5.15 ENiFe-CI

Storage儲存：Electrodes should be stored in dry conditions. Should the electrodes become damp, re-dry for one hour at 150°C before use. 焊條應(yīng)儲存在干燥環(huán)境中。如果焊條受潮，應(yīng)在150°C下重新干燥1小時(shí)后再使用。

使用注意事項(xiàng)：

如有可能，清潔焊接區(qū)域。去除表皮和所有銳邊。確保施焊部位沒有油污等。

推薦采用“U”坡口接頭。

使用3mm鉆頭在裂縫末端鉆孔，以防止焊接過程中進(jìn)一步擴(kuò)展。

從裂縫的末端開始焊接，向內(nèi)焊接。

使用低電流并保持短弧。

應(yīng)使用短線狀焊道(2-3cm)或窄編織焊道，以防止過熱。

采用直流焊機(jī)時(shí)根據(jù)熔敷情況改變正負(fù)極。

斷開電弧時(shí)，始終填充弧坑，并將焊條拉回到焊縫熔敷層上。

趁熱錘擊將有助于降低收縮應(yīng)力。

重新引弧時(shí)，電弧從先前沉積的焊縫金屬開始，而不是從母材開始。

讓零件慢慢冷卻。